产品简介: |
抗蠕变低合金钢电焊条(smaw electrodes for creep resistant low-alloyed steels)
|
产品牌号
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a…
|
en…
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
s≤
|
p≤
|
cu≤
|
mpa
|
mpa
|
%
|
℃
|
j
|
sh schwarz 3 t
|
5.5:
|
e8013-g
|
1599:
|
e mo r 12
|
0.09
|
0.60
|
0.25
|
-
|
0.45
|
-
|
0.030
|
0.025
|
-
|
sr
|
460
|
550
|
22
|
+20
|
55
|
sh schwarz 3 tr
|
5.5:
|
e8013-g
|
1599:
|
e mo r 12
|
0.08
|
0.55
|
0.25
|
-
|
0.50
|
-
|
0.025
|
0.025
|
-
|
sr
|
430
|
520
|
22
|
+20
|
55
|
sh kupfer 1 tr
|
5.5:
|
e8013-g
|
1599:
|
e crmo 1 r 12
|
0.10
|
0.65
|
0.20
|
0.90
|
0.50
|
-
|
0.030
|
0.020
|
-
|
sr
|
350
|
490
|
22
|
+20
|
70
|
phoenix blau mo
|
5.5:
|
e7011-a1
|
1599:
|
e mo r 11
|
0.10
|
0.50
|
0.35
|
-
|
0.45
|
-
|
0.030
|
0.025
|
-
|
aw
|
420
|
510
|
22
|
+20
|
55
|
sh schwarz 3 k
|
5.5:
|
e7015-g
(~a1)
|
1599:
|
e mob 42 h5
|
0.08
|
1.20
|
0.30
|
-
|
0.45
|
-
|
0.025
|
0.025
|
-
|
sr
|
480
|
550
|
21
|
-40
|
47
|
sh schwarz 3 kr
|
5.5:
|
e7015-g
(~a1)
|
1599:
|
e mob 42 h5
|
0.09
|
1.15
|
0.55
|
-
|
0.45
|
-
|
0.025
|
0.025
|
-
|
sr
|
460
|
530
|
21
|
-40
|
47
|
sh schwarz 3 mk
|
5.5:
|
e7018-g
(~a1)
|
1599:
|
e mob 42 h5
|
0.06
|
1.20
|
0.35
|
-
|
0.45
|
-
|
0.025
|
0.025
|
-
|
sr
|
480
|
550
|
21
|
-40
|
47
|
sh schwarz 3 k ni
|
5.5:
|
e9018-g
|
499:
|
e 50 4 1 nimo b 42 h5
|
0.06
|
1.25
|
0.30
|
-
|
0.40
|
0.95
|
0.01
|
0.01
|
0.08
|
sr
|
500
|
590
|
21
|
-40
|
47
|
thyssen nimo 100
|
5.5:
|
e10018-g
(~d2)
|
757:
|
e 62 4 mn 1 nimo b 42 h5
|
0.11
|
1.85
|
0.25
|
-
|
0.40
|
0.95
|
0.020
|
0.020
|
-
|
sr
|
600
|
690
|
18
|
-40
|
47
|
|
产品牌号
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws 5.5:
|
en1599:
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
w
|
nb
|
v
|
mpa
|
mpa
|
%
|
℃
|
j
|
phoenix chromo 1 k
|
e8018-b2
|
e crmo 1 b 42 h5
|
0.06
|
0.90
|
0.30
|
1.00
|
0.50
|
-
|
-
|
-
|
-
|
sr1
|
490
|
580
|
22
|
+20
|
110
|
thyssen chromo 1
|
e8018-b2
|
e crmo 1 b 42 h5
|
0.06
|
0.85
|
0.25
|
1.20
|
0.50
|
-
|
-
|
-
|
-
|
sr2
|
450
|
540
|
22
|
-40
|
60
|
sh kupfer 1 k
|
e8018-b2
|
e crmo 1 b 42 h5
|
0.06
|
0.90
|
0.30
|
1.00
|
0.50
|
-
|
-
|
-
|
-
|
sr1
|
490
|
580
|
22
|
+20
|
110
|
sh kupfer 1 kc
|
e8018-g(~b2)
|
ez crmo 1 b 42 h5
|
0.13
|
0.90
|
0.30
|
1.00
|
0.50
|
-
|
-
|
-
|
-
|
sr2
|
400
|
600
|
20
|
±0
|
50
|
sh kupfer 3 k
|
e9015-g
|
e crmo 1 b 42 h5
|
0.06
|
1.10
|
0.25
|
1.10
|
1.00
|
-
|
-
|
-
|
0.28
|
sr1
|
500
|
600
|
20
|
±0
|
50
|
sh kupfer 3 kc
|
e9015-g
|
ez crmov 1 b 42 h5
|
0.13
|
1.00
|
0.40
|
1.40
|
1.05
|
-
|
-
|
-
|
0.25
|
sr1
|
520
|
630
|
18
|
+20
|
40
|
sh chromo 2 ks
|
e9015-b3
|
e crmo 2 b 42 h5
|
0.07
|
0.70
|
0.25
|
2.20
|
0.90
|
-
|
-
|
-
|
-
|
sr1
|
440
|
550
|
22
|
-40
|
80
|
thyssen chromo 2 v
|
e9015-g
|
e crmo 2 v b 42 h5
|
0.09
|
0.75
|
0.25
|
2.50
|
1.00
|
-
|
-
|
-
|
0.25
|
sr9
|
540
|
670
|
18
|
-40
|
55
|
thyssen chromo 3 v
|
e9015-g
|
e crmo 3 v b 42 h5
|
0.09
|
0.60
|
0.20
|
3.00
|
1.00
|
-
|
-
|
-
|
0.25
|
sr9
|
570
|
700
|
18
|
-40
|
55
|
thyssen chromo 5
|
e8015-b6
|
e crmo 5 b 42 h5
|
0.06
|
0.90
|
0.30
|
5.00
|
0.50
|
-
|
-
|
-
|
-
|
sr1
|
490
|
620
|
19
|
+20
|
70
|
thyssen chromo 9 v
|
e9015-b9
|
e crmo 9 1 b 42 h5
|
0.09
|
0.60
|
0.20
|
9.00
|
1.10
|
0.80
|
-
|
0.05
|
0.20
|
sr3
|
530
|
620
|
17
|
+20
|
47
|
thyssen chromo t 91
|
e9015-b9
|
-
|
0.09
|
0.60
|
0.30
|
9.00
|
1.00
|
0.80
|
-
|
0.05
|
0.20
|
sr3
|
530
|
620
|
17
|
+20
|
47
|
thermanit mts 4
|
-
|
e crmowv 12 b 42 h5
|
0.18
|
0.60
|
0.30
|
11.0
|
1.00
|
0.60
|
0.50
|
-
|
0.30
|
sr3
|
590
|
700
|
15
|
+20
|
35
|
thermanit mts 616
|
e9015-g(~b9)
|
ez crmowv 9 0.5 2 b 42 h5
|
0.11
|
0.60
|
0.20
|
8.80
|
0.50
|
0.70
|
1.60
|
0.05
|
0.20
|
sr3
|
560
|
720
|
15
|
+20
|
41
|
thermanit mts 911
|
e9015-g(~b9)
|
e crmo 9 1 1 b 42 h5
|
0.11
|
0.60
|
0.25
|
8.80
|
1.00
|
0.70
|
1.00
|
0.05
|
0.20
|
sr3
|
560
|
720
|
15
|
+20
|
41
|
|
细晶粒低合金结构钢电焊条 (fine grained low-alloyed structural steels smaw electrode)
产品牌号
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a…
|
en…
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
s≤
|
p≤
|
cu≤
|
mpa
|
mpa
|
%
|
℃
|
j
|
phoenix 120 k
|
5.1:
|
e7018-1
|
499:
|
e 42 5 b 32 h5
|
0.07
|
1.20
|
0.35
|
-
|
-
|
-
|
0.020
|
0.020
|
-
|
sr
|
400
|
500
|
26
|
-50
|
47
|
sh grün k 70
|
5.5:
|
e8018-g
|
499:
|
e 46 4 b 42 h5
|
0.07
|
1.60
|
0.35
|
-
|
-
|
-
|
0.020
|
0.020
|
-
|
sr
|
450
|
520
|
25
|
-40
|
47
|
sh schwarz 3 k
|
5.5:
|
e7015-g
(~a1)
|
1599:
|
e mob 42 h5
|
0.08
|
1.20
|
0.30
|
-
|
0.45
|
-
|
0.025
|
0.025
|
-
|
sr
|
480
|
550
|
21
|
-40
|
47
|
sh schwarz 3 mk
|
5.5:
|
e7018-g
(~a1)
|
1599:
|
e mob 42 h5
|
0.06
|
1.20
|
0.35
|
-
|
0.45
|
-
|
0.025
|
0.025
|
-
|
sr
|
480
|
550
|
21
|
-40
|
47
|
sh schwarz 3 k ni
|
5.5:
|
e9018-g
|
499:
|
e 50 4 1 nimo b 42 h5
|
0.06
|
1.25
|
0.30
|
-
|
0.40
|
0.95
|
0.01
|
0.01
|
0.08
|
sr
|
500
|
590
|
21
|
-40
|
47
|
sh v 370
|
5.5:
|
e8018-c3
|
499:
|
e 46 6 1 ni b 42 h5
|
0.06
|
1.15
|
0.25
|
-
|
-
|
0.95
|
0.020
|
0.020
|
-
|
sr
|
420
|
510
|
26
|
-60
|
50
|
sh v 1
|
5.5:
|
e8018-g
(~c3)
|
499:
|
e 50 6 mn 2 ni b 42 h5
|
0.07
|
1.50
|
0.25
|
-
|
-
|
0.95
|
0.020
|
0.020
|
-
|
sr
|
470
|
560
|
25
|
-60
|
50
|
sh ni 2 k 70
|
5.5:
|
e8018-c1
|
499:
|
e 46 6 2 ni b 42 h5
|
0.06
|
1.15
|
0.30
|
-
|
-
|
2.10
|
0.020
|
0.020
|
-
|
sr
|
450
|
540
|
28
|
-80
|
47
|
sh ni 2 k 90
|
5.5:
|
e10018-m
|
757:
|
e 55 5 nimo b 42 h5
|
0.06
|
1.40
|
0.25
|
-
|
0.44
|
1.70
|
0.025
|
0.025
|
-
|
sr
|
570
|
650
|
21
|
-50
|
47
|
sh ni 2 k 100
|
5.5:
|
e11018-m
|
757:
|
e 69 5 mn 2 nicrmo b 42 h5
|
0.06
|
1.60
|
0.20
|
0.38
|
0.40
|
1.85
|
0.025
|
0.025
|
-
|
sr
|
690
|
740
|
19
|
-50
|
47
|
sh ni 2 k 130
|
5.5:
|
e12018-g
(~m)
|
757:
|
e 89 4 mn 2 ni 1crmo b 42 h5
|
0.06
|
1.30
|
0.40
|
0.80
|
0.65
|
2.20
|
0.020
|
0.020
|
-
|
aw
|
880
|
920
|
18
|
-45
|
90
|
低温钢实心、药芯焊丝(low-alloyed structural steels gtaw rods/wires, gmaw, fcaw and mcaw wires)
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a…
|
en…
|
c
|
mn
|
si
|
ni
|
s≤
|
p≤
|
al
|
cr
|
mo
|
mpa
|
mpa
|
%
|
℃
|
j
|
union i 1,2 ni
|
gtaw
|
5.28:
|
er80s-g
|
1668:
|
w3ni1
|
0.10
|
1.40
|
0.70
|
1.30
|
0.020
|
0.020
|
-
|
-
|
-
|
aw
|
490
|
590
|
25
|
-60
|
65
|
union i 5 ni
|
gmaw
|
5.28:
|
er80s-g
|
440:
|
g463cg3ni1/g505mg3ni1
|
0.10
|
1.40
|
0.70
|
1.40
|
0.020
|
0.020
|
-
|
-
|
-
|
aw
|
490
|
600
|
25
|
-50
|
50
|
union i 2,5 ni
|
gtaw
|
5.28:
|
er80s-ni2
|
1668:
|
w2ni2
|
0.08
|
1.00
|
0.60
|
2.35
|
0.020
|
0.020
|
-
|
-
|
-
|
sr
|
440
|
540
|
26
|
-90
|
45
|
union ni 2,5
|
gmaw
|
5.28:
|
er80s-ni2
|
440:
|
g506mg2ni2
|
0.08
|
1.00
|
0.60
|
2.35
|
0.020
|
0.020
|
-
|
-
|
-
|
sr
|
450
|
560
|
24
|
-80
|
55
|
|
高强钢实心焊丝(high tensile steels gtaw rods/wires and gmaw wires)
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a5.28:
|
g en 12534:
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
s≤
|
p≤
|
cu
|
mpa
|
mpa
|
%
|
℃
|
j
|
union moni
|
gmaw
|
er90s-g
|
g mn3ni1mo
|
0.10
|
1.55
|
0.65
|
|
0.40
|
1.10
|
0.015
|
0.015
|
-
|
aw
|
620
|
700
|
18
|
-60
|
40
|
union nimocr
|
gmaw
|
er100s-g(~1)
|
g mn4ni1,5crmo
|
0.08
|
1.70
|
0.60
|
0.20
|
0.50
|
1.50
|
0.015
|
0.015
|
-
|
aw
|
720
|
780
|
16
|
-60
|
45
|
union x 85
|
gmaw
|
er110s-g
|
g mn4ni1,5crmo
|
0.09
|
1.70
|
0.70
|
0.30
|
0.60
|
1.85
|
0.015
|
0.015
|
-
|
aw
|
770
|
880
|
16
|
-50
|
45
|
union x 90
|
gmaw
|
er120s-g
|
g mn4ni2crmo
|
0.10
|
1.80
|
0.80
|
0.35
|
0.60
|
2.30
|
0.015
|
0.015
|
-
|
aw
|
890
|
950
|
15
|
-40
|
50
|
union x 96
|
gmaw
|
er120s-g
|
g mn4ni2,5crmo
|
0.12
|
1.90
|
0.80
|
0.45
|
0.55
|
2.35
|
0.015
|
0.015
|
-
|
aw
|
930
|
980
|
14
|
-40
|
40
|
|
抗蠕变钢实心、药芯焊丝(creep resistant low-alloyed steels gtaw rods/wires, gmaw,fcaw and mcaw wires)
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a5.28:
|
en…
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
nb
|
w
|
v
|
mpa
|
mpa
|
%
|
℃
|
j
|
union i mo
|
gtaw
|
er80s-g
|
1668:
12070:
|
w2mo
w mosi
|
0.10
|
1.15
|
0.60
|
-
|
0.50
|
-
|
-
|
-
|
-
|
aw
|
480
|
570
|
23
|
+20
|
110
|
union i mo*
|
gmaw
|
er80s-g
|
440:
12070:
|
g2mo
g mosi
|
0.10
|
1.15
|
0.60
|
-
|
0.50
|
-
|
-
|
-
|
-
|
aw
|
490
|
600
|
23
|
+20
|
90
|
thyssen mv mo*
|
mcaw
|
er80c-g h4
|
758:
12071:
|
t 46 2 mo m m 2 h5
t mo mm 2 h5
|
0.06
|
1.0
|
0.35
|
-
|
0.5
|
-
|
-
|
-
|
-
|
aw
|
490
|
560
|
22
|
+20
|
100
|
*:保护气体为m21(氩气+15至25%co2) |
产品牌号
|
类别
|
分类标准及标号
|
<div a, , l |
|
|
低温钢实心、药芯焊丝(low-alloyed structural steels gtaw rods/wires, gmaw, fcaw and mcaw wires)
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a…
|
en…
|
c
|
mn
|
si
|
ni
|
s≤
|
p≤
|
al
|
cr
|
mo
|
mpa
|
mpa
|
%
|
℃
|
j
|
union i 1,2 ni
|
gtaw
|
5.28:
|
er80s-g
|
1668:
|
w3ni1
|
0.10
|
1.40
|
0.70
|
1.30
|
0.020
|
0.020
|
-
|
-
|
-
|
aw
|
490
|
590
|
25
|
-60
|
65
|
union i 5 ni
|
gmaw
|
5.28:
|
er80s-g
|
440:
|
g463cg3ni1/g505mg3ni1
|
0.10
|
1.40
|
0.70
|
1.40
|
0.020
|
0.020
|
-
|
-
|
-
|
aw
|
490
|
600
|
25
|
-50
|
50
|
union i 2,5 ni
|
gtaw
|
5.28:
|
er80s-ni2
|
1668:
|
w2ni2
|
0.08
|
1.00
|
0.60
|
2.35
|
0.020
|
0.020
|
-
|
-
|
-
|
sr
|
440
|
540
|
26
|
-90
|
45
|
union ni 2,5
|
gmaw
|
5.28:
|
er80s-ni2
|
440:
|
g506mg2ni2
|
0.08
|
1.00
|
0.60
|
2.35
|
0.020
|
0.020
|
-
|
-
|
-
|
sr
|
450
|
560
|
24
|
-80
|
55
|
|
高强钢实心焊丝(high tensile steels gtaw rods/wires and gmaw wires)
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a5.28:
|
g en 12534:
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
s≤
|
p≤
|
cu
|
mpa
|
mpa
|
%
|
℃
|
j
|
union moni
|
gmaw
|
er90s-g
|
g mn3ni1mo
|
0.10
|
1.55
|
0.65
|
|
0.40
|
1.10
|
0.015
|
0.015
|
-
|
aw
|
620
|
700
|
18
|
-60
|
40
|
union nimocr
|
gmaw
|
er100s-g(~1)
|
g mn4ni1,5crmo
|
0.08
|
1.70
|
0.60
|
0.20
|
0.50
|
1.50
|
0.015
|
0.015
|
-
|
aw
|
720
|
780
|
16
|
-60
|
45
|
union x 85
|
gmaw
|
er110s-g
|
g mn4ni1,5crmo
|
0.09
|
1.70
|
0.70
|
0.30
|
0.60
|
1.85
|
0.015
|
0.015
|
-
|
aw
|
770
|
880
|
16
|
-50
|
45
|
union x 90
|
gmaw
|
er120s-g
|
g mn4ni2crmo
|
0.10
|
1.80
|
0.80
|
0.35
|
0.60
|
2.30
|
0.015
|
0.015
|
-
|
aw
|
890
|
950
|
15
|
-40
|
50
|
union x 96
|
gmaw
|
er120s-g
|
g mn4ni2,5crmo
|
0.12
|
1.90
|
0.80
|
0.45
|
0.55
|
2.35
|
0.015
|
0.015
|
-
|
aw
|
930
|
980
|
14
|
-40
|
40
|
|
抗蠕变钢实心、药芯焊丝(creep resistant low-alloyed steels gtaw rods/wires, gmaw,fcaw and mcaw wires)
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a5.28:
|
en…
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
nb
|
w
|
v
|
mpa
|
mpa
|
%
|
℃
|
j
|
union i mo
|
gtaw
|
er80s-g
|
1668:
12070:
|
w2mo
w mosi
|
0.10
|
1.15
|
0.60
|
-
|
0.50
|
-
|
-
|
-
|
-
|
aw
|
480
|
570
|
23
|
+20
|
110
|
union i mo*
|
gmaw
|
er80s-g
|
440:
12070:
|
g2mo
g mosi
|
0.10
|
1.15
|
0.60
|
-
|
0.50
|
-
|
-
|
-
|
-
|
aw
|
490
|
600
|
23
|
+20
|
90
|
thyssen mv mo*
|
mcaw
|
er80c-g h4
|
758:
12071:
|
t 46 2 mo m m 2 h5
t mo mm 2 h5
|
0.06
|
1.0
|
0.35
|
-
|
0.5
|
-
|
-
|
-
|
-
|
aw
|
490
|
560
|
22
|
+20
|
100
|
*:保护气体为m21(氩气+15至25%co2) |
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a…
|
en…
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
nb
|
w
|
v
|
mpa
|
mpa
|
%
|
℃
|
j
|
union i crmo
|
gtaw
|
5.28:
|
er80s-g
|
12070:
|
w crmo 1 si
|
0.10
|
1.00
|
0.60
|
1.10
|
0.50
|
-
|
-
|
-
|
-
|
sr1
|
450
|
560
|
22
|
+20
|
90
|
union i crmo*
|
gmaw
|
5.28:
|
er80s-g
|
12070:
|
g crmo 1 si
|
0.09
|
1.05
|
0.60
|
1.10
|
0.50
|
-
|
-
|
-
|
-
|
sr1
|
450
|
560
|
22
|
+20
|
80
|
thyssen mv crmo
|
mcaw
|
5.28:
|
e80c-b2 h4
|
12071:
|
t crmo 1 mm 2 h5
|
0.07
|
1.0
|
0.35
|
1.00
|
0.50
|
-
|
-
|
-
|
-
|
sr1
|
470
|
560
|
20
|
+20
|
100
|
union i crmo 910
|
gtaw
|
5.28:
|
er90s-g
|
12070:
|
w crmo 2 si
|
0.07
|
1.00
|
0.60
|
2.55
|
1.00
|
-
|
-
|
-
|
-
|
sr1
|
470
|
590
|
20
|
+20
|
80
|
union i crmo 910*
|
gmaw
|
5.28:
|
er90s-g
|
12070:
|
g crmo 2 si
|
0.09
|
0.90
|
0.55
|
2.55
|
1.00
|
-
|
-
|
-
|
-
|
sr1
|
460
|
570
|
20
|
+20
|
65
|
union i cr 2 wv
|
gtaw
|
5.28:
|
er90s-g
|
12070:
|
w zcrwv2
|
0.07
|
0.5
|
0.3
|
2.2
|
-
|
-
|
-
|
1.7
|
0.22
|
aw
|
850
|
950
|
-
|
+20
|
30
|
union i cr 2 wv*
|
gmaw
|
5.28:
|
er90s-g
|
12070:
|
g zcrwv2
|
0.07
|
0.5
|
0.3
|
2.2
|
-
|
-
|
-
|
1.7
|
0.22
|
aw
|
850
|
950
|
-
|
+20
|
30
|
union i crmovti b
|
gtaw
|
5.28:
|
er90s-g
|
12070:
|
w zcrmov2
|
0.05
|
0.5
|
0.3
|
2.2
|
1.0
|
ti:0.05
|
b:0.003
|
-
|
0.22
|
740℃/2h
|
500
|
600
|
20
|
+20
|
180
|
union i crmovti b*
|
gmaw
|
5.28:
|
er90s-g
|
12070:
|
g zcrmov2
|
0.05
|
0.5
|
0.3
|
2.2
|
1.0
|
ti:0.05
|
b:0.003
|
-
|
0.22
|
740℃/2h
|
500
|
600
|
20
|
+20
|
180
|
union i crmo 5
|
gtaw
|
5.28:
|
er80s-b6
|
12070:
|
w crmo 5 si
|
0.08
|
0.55
|
0.35
|
6.00
|
0.65
|
-
|
-
|
-
|
-
|
sr1
|
450
|
570
|
18
|
+20
|
100
|
union i crmo 5*
|
gmaw
|
5.28:
|
er80s-b6
|
12070:
|
g crmo 5 si
|
0.08
|
0.55
|
0.35
|
6.00
|
0.65
|
-
|
-
|
-
|
-
|
sr1
|
450
|
550
|
18
|
+20
|
100
|
thermanit mts 3
|
gtaw
|
5.28:
|
er90s-b9
|
12070:
|
w crmo 9 1
|
0.10
|
0.50
|
0.30
|
9.00
|
1.00
|
0.70
|
0.06
|
-
|
0.20
|
sr4
|
520
|
620
|
16
|
+20
|
50
|
thermanit mts 3*
|
gmaw
|
5.28:
|
er90s-b9
|
12070:
|
g crmo 9 1
|
0.10
|
0.50
|
0.30
|
9.00
|
1.00
|
0.70
|
0.06
|
-
|
0.20
|
sr4
|
520
|
620
|
16
|
+20
|
50
|
thermanit mts 3 fd*
|
mcaw
|
5.28:
|
e90c-b9 h4
|
12071:
|
t zm m 2 h5
|
0.09
|
0.75
|
0.2
|
9.0
|
1.1
|
0.65
|
0.04
|
-
|
0.2
|
sr4
|
550
|
680
|
16
|
+20
|
47
|
thermanit mts 4 si
|
gtaw
|
-
|
-
|
12070:
|
w crmowv 12 si
|
0.20
|
0.60
|
0.30
|
11.0
|
1.00
|
0.40
|
-
|
0.50
|
0.30
|
sr3
|
590
|
700
|
15
|
+20
|
35
|
thermanit mts 4 si*
|
gmaw
|
5.9:
|
≈er505
|
12070:
|
g crmowv 12 si
|
0.20
|
0.60
|
0.30
|
11.0
|
1.00
|
0.40
|
-
|
0.50
|
0.30
|
sr3
|
590
|
700
|
15
|
+20
|
35
|
thermanit mts 616
|
gtaw
|
5.28:
|
er90s-g
|
12070:
|
w z crmowvnb 9 0.5 1.5
|
0.10
|
0.45
|
0.38
|
8.80
|
0.50
|
0.70
|
0.06
|
1.6
|
0.20
|
sr3
|
560
|
720
|
16
|
+20
|
41
|
thermanit mts 616*
|
gmaw
|
5.28:
|
er90s-g
|
12070:
|
g z crmowvnb 9 0.5 1.5
|
0.10
|
0.45
|
0.38
|
8.80
|
0.40
|
0.60
|
0.06
|
1.6
|
0.20
|
sr3
|
560
|
720
|
16
|
+20
|
41
|
thermanit mts 911
|
gtaw
|
5.28:
|
er90s-g
|
12070:
|
w z crmowvnb 9 1 1
|
0.10
|
0.45
|
0.38
|
9.00
|
1.00
|
0.70
|
0.06
|
1.00
|
0.20
|
sr3
|
560
|
720
|
16
|
+20
|
41
|
thermanit mts 911*
|
gmaw
|
5.28:
|
er90s-g
|
12070:
|
g z crmowvnb 9 1 1
|
0.10
|
0.45
|
0.38
|
9.00
|
1.00
|
0.70
|
0.06
|
1.00
|
0.20
|
sr3
|
560
|
720
|
16
|
+20
|
41
|
|
耐大气腐蚀钢实心焊丝(weatherproof steels gmaw wires)
产品牌号
|
类别
|
分类标准及标号
|
基本化学成份典型值(%)
|
热处理
|
σ0.2
|
σb
|
δ5
|
akw
|
aws a…
|
en
|
c
|
mn
|
si
|
cr
|
mo
|
ni
|
s≤
|
p≤
|
cu
|
mpa
|
mpa
|
%
|
℃
|
j
|
union patinax**
|
gmaw
|
5.18:
|
er70s-g
|
440:
|
g423cg0/g464mg0
|
0.09
|
1.50
|
0.85
|
-
|
-
|
0.50
|
0.020
|
0.020
|
0.40
|
aw
|
480
|
590
|
24
|
-40
|
50
|
*保护气体为m21(氩气+15至25%co2)
|
**:可使用混合气体或纯co2保护,但使用co2保护时的机械性能有所变化
|
|
|